of jamesonite is also dependent on the pulp potential. The potential-pH range for jamesonite flotation is established. The FTIR spectroscopy analysis shows that the major adsorption product of sodium... are correlated with the pulp potential.
Key words: jamesonite; flotation behavior; floatability diethyldithiocarbamate; electrochemical flotation; FTIR spectroscopy
through BET (Brunauer-Emmett-Teller-N2) surface area analysis, BJH (Barrett-Joyner-Halenda) pore volume analysis, SEM (scanning electron microscopy), FTIR (Fourier transform infrared spectroscopy...;FTIR分析 中图分类号:X703.1 文献标志码:A 文章编号:1672-7207(2017)03-0570-08 Preparation and properties analysis of biochars......人粪生物炭的制备及性能分析
来源: 《中南大学学报(自然科学版)2017年第3期》——李子富 白晓凤 张耀中 倪结文 云玉攀 尹福斌
investigated under the operational conditions of pressure of 1 kPa, oil bath temperature of 210-230 ℃, and outlet temperature of 190 ℃. The condensate sample was characterized by FTIR, 1H-NMR spectroscopy... produced in Germany with Ar atmosphere protection. 2.3 Characterization FTIR spectroscopy of condensate and distilled residue was measured with a Perkin Elmer 2000 IR spectrometer. Raman spectra were......
苯乙烯/马来酸酐共聚物的氢键诱导液晶化 李伯耿1,晏华1,潘祖仁1 (1.浙江大学聚合反应工程国家重点实验室,杭州,310027) 摘要:制备了以苯乙烯/马来酸-4-羧基酚酯共聚物(ME-SMA)为质子供体,苯乙烯基吡啶(4SZ)为质子受体的氢键诱导液晶复合物.用DSC和POM研究二者复合前后的液晶行为.结果表明,4SZ含量在30%~70%的复合物表现为向列相液晶态,其中等摩尔比的复合物的热稳定性最高.并从IR结果讨论了ME-SMA/4SZ二元组分的摩尔比与分子间氢键的关系,等摩尔比时,复合物以羧酸与吡啶环之间的氢键为主;而非等摩尔比时,存在羧酸之间的氢键. 关键词:苯乙烯/马来酸酐共......
苯乙烯-马来酸酐共聚物/金纳米微粒的合成陈延明,樊晓辉,司春雷摘 要:以氯金酸为原料,DMF(N,N-二甲基甲酰胺)为溶剂及还原剂,苯乙烯-马来酸酐共聚物为大分子稳定剂,合成了金纳米微粒.通过紫外-可见吸收光谱,透射电子显微镜等方法对纳米金样品进行了表征.结果表明:所得到的金纳米微粒可以在520 nm530 nm范围内产生明显的纳米金所具有的特征等离子共振吸收峰,金纳米微粒的尺寸在3 nm5nm且具有较窄的分布,证明苯乙烯-马来酸酐共聚物可以对金纳米微粒表面产生较好的修饰作用,从而为制备纳米金材料提供了一种......
on pulp potential at certain pH value. The potential-pH range for pyrrhotite flotation was established. Cyclic voltammetry and FTIR spectroscopy analysis show that the major adsorption product... are correlated with pulp potentials. Key words: ethyl xanthate; pyrrhotite; electrochemical flotation; FTIR spectroscopy; cyclic voltammetry CLC number: TD952 Document code: A 1 INTRODUCTION......
苯乙烯-马来酸酐共聚物固化氰酸酯改性环氧体系反应动力学研究 王敬锋1,苏民社1,杨中强1,孔凡旺1 (1.广东生益科技有限公司,广东,东莞,523039) 摘要:采用非等温差示扫描量热法(DSC)研究了氰酸酯/环氧树脂/苯乙烯-马来酸酐共聚物(CE/EP/SMA)三元体系的固化反应动力学.通过线性回归分析得到了不同升温速率下,固化反应的凝胶化温度(Ti),固化温度(Tp)和后处理温度(Tt).根据Kissinger方法,求得表观活化能为63.71 kJ/mol;根据Flynn-Wall-Oza-wa法,得到反应表观活化能为68.07kJ/mol;根据Crane方程,得到反应级数为0.89......
一种改性磺化苯乙烯/马来酸酐共聚物的合成及阻垢杀菌性能研究朱驯1,2,项东升1,周玲2,31. 盐城纺织职业技术学院化工系2. 南京理工大学化工学院3. 中国电子科技集团第二十八研究所摘 要:以马来酸酐(MA),对苯乙烯磺酸钠(SS)和N,N-二甲基-N-苄基-N-丙烯酸酯基氯化铵(DA)为单体,K2S2O8作为引发剂,在水相中合成共聚物阻垢剂P(MA-SS-DA).通过正交实验,确定了合成P(MA-SS-DA)的最佳条件为:n(MA)∶n(SS)∶n(DA)=1∶0.6∶0.2,聚合温度为80℃,K2S2......
有机硅改性苯乙烯-马来酸酐共聚物的性能研究宋建华,吕澍,苏育志摘 要:以乙酸乙酯为溶剂,采用溶液聚合方法,分别添加5%,10%,15%,20%,25%,30%和35%硅烷偶联剂(KH-570)与苯乙烯,马来酸酐共聚反应得到一系列有机硅改性的SMA共聚物;并探讨了改性前后产物在各种溶剂中的溶解度,水解产物的粘度,红外光谱以及热分析谱图的变化.实验结果表明:通过KH-570改性后的SMA共聚物发生交联反应使聚合物分子量变大,溶解度降低,热失重温度以及玻璃化温度Tg升高.关键词:苯乙烯;马来酸酐;K......
苯乙烯-马来酸酐共聚物/氧化锌纳米粒子合成与表征陈延明,贾宏伟沈阳工业大学石油化工学院摘 要:以N,N-二甲基甲酰胺为溶剂,乙酸锌为前驱物,苯乙烯-马来酸酐共聚物为大分子稳定剂,采用溶液化学法,制备了氧化锌纳米粒子.通过紫外-可见吸收光谱(UV-Vis),荧光光谱(PL),透射电子显微镜(TEM)等方法对合成的ZnO纳米粒子样品进行表征.结果表明,所合成样品具有量子尺寸效应,样品UV-Vis吸收光谱在350nm给出氧化锌纳米粒子的特征吸收峰,样品PL光谱显示在410nm处可产生明显的荧光发射.氧化锌纳米粒子......